Calor curatio de Aluminium Alloy Die Castings est control ad calefactio celeritate ad correspondentes temperatus, et tunc calidum ad certum tempus et tunc refrigescant quod ad rate . hoc potest mutare et stabilitatem {I}} Quid est calor curatio technology, {I}} Quid est calor technology processibus, et emendare, et stabilitatem {I}} Quid est calor technology processuum, et emendare, {I}} Quid est calor treatment technology, et emendare} {IMPECTATIONE EST} {IMPECTATIO EST Taedet Technology Processes I} Quid est quod calor technology, et emendare} {IMPECTATIO EST} {IMPECTATIO EST Taedet Technology (I}}
, 1. senescit processus
After quenching, the strength and hardness of aluminum alloy die castings will be significantly improved after standing for a period of time, while the plasticity will be significantly reduced. The phenomenon that the strength and hardness of aluminum alloy die castings after quenching increase significantly with time is called aging. Aging can occur at room temperature, called natural aging, or it can occur in a certain temperature range above room Temperature, dicitur artificialis senatus {{II}}
{{{0} Confortat principium Aluminium Alloy
When aluminum alloy die castings are quenched and heated, vacancies are formed in the alloy. During quenching, due to rapid cooling, these vacancies have no time to move out and are "fixed" in the crystal. Most of these vacancies in the supersaturated solid solution are combined with solute atoms. Since the supersaturated solid solution is in an unstable state, it will Altera mutare ad aequilibrium statu {{III}} quod est ex Vicancies accelerat ad diffusionem rate of solute atomorum, ita accelerans segregationem solute atomorum {{}}
Et magnitudine et numerus durae zonas aluminium mixturae mori castings dependet in extinguendo temperatus et extinguat refrigerationem rate . superiori in solidam, quod est magis in solido, quod est in solidam, quod est magis in solido, quod est in solitudine, quod est magis in solido, quod est in solidum, quod est in solidam augendae numerum obfirmatus zonas Aluminium Mimey Die Castings et reducendo magnitudinem ad duram zonas {{II}}