1. It is very troublesome to clean the mold parting surface. It is easy to ignore. If the boss has a high starting point and buy a good mold, it will be much easier to work. If the mold quality is not good, the production will be poor. When there is inevitably a flash or dirt on the mold parting surface, the operator should always clean these parts and equip with a small blade at any Tempus {{V}} si Flash Edge non amoveatur in tempore, et fingunt dividitur superficies est facile ad ruina, causando aluminium ad currere in productione processus {{VI} cum hoc non solum ex eo quod non solum}} exeundi, sed etiam in albis aluminum, the quality of the product is also unstable, especially the internal quality, and the difficulty of determining the process parameters is increased. The qualification rate will drop a lot. From the safety point of view, Increased the chance of a work-related injury. At the time of handover, the operator thoroughly cleans the mold parting surface by applying kerosene, which not only prevents the mold from being crushed, but also can clean the mold Per residuum de release agente vel alii lutum {}}}}} et gas canalibus aperitur, quod est utile ad Gas defluxiones in cavum in iniectio processus ut amplio qualis est ex parte {{}} {{{}}}}}
2. Use of mold cooling system. Mold cooling water not only prolongs the service life of the mold but also improves production efficiency when used correctly. In actual production, we often overlook the importance of it, the operators also save trouble, pick up and take too much trouble, do not pick up the cooling water pipe, and some companies even do not cool in order to save costs when customizing the mold Water, which has serious {{III}} et materiae formae sunt plerumque facta est specialis fingunt in varias treatments {{}} etiam optimum fingunt, ut non est in usu, si non est in inauri, {{}} etsi non est in in magnam}} {et in inaugurare, ut non est in magna in quadratum, quod est in quadam, ut non est in magna ex area et in quadam, {VII}} molds, because the mold temperature is too high, the core has changed color, and even after measuring more than 400 degrees, such a temperature is prone to cracking of the turtle when the mold release agent is chilled, and the product is produced. It is also prone to deformation, strain, and sticking. In the case of using mold cooling water, the use of the release agent can be greatly reduced, so that the operator does not use the Release agente ad inferiora temperatus ad fusi} {{XI}} utilitatem exemplar habet commoda efficaciter extendendo ad vitam fingunt, salvis, ut exiguam, et reducendo ad haerentem et exhauriat, {}}}}}